High Temperature CeramicsDepartment

The working temperature of ultra high temperature ceramics are more than 1800 degrees.They are widely used in aerospace, high temperature alloy, special noble metal, high temperature chemical, artificial crystal and other industrial fields.

Alumina Ceramics

Technical parameters:

Content:99-99.7%Density:3.90g/cm3
Compressive strength:2600 MpaBending strength:379 Mpa
Thermal shock resistance :GoodMax serve temp:1800-2000℃

Zirconia Ceramics

Technical parameters:

Content:99%Density:6.01g/cm3
Compressive strength:2600 MpaBending strength:900 Mpa
Thermal shock resistance :GoodMax serve temp:2300-2400℃

Magnesia Ceramics

下载捕鱼游戏Technical parameters:

Content:99%Density:3.50g/cm3
Compressive strength:1800 MpaBending strength:600 Mpa
Thermal shock resistance :GoodMax serve temp:2200℃

Silicon Carbide Ceramics

下载捕鱼游戏Technical parameters:

Content:99%Density:3.02g/cm3
Compressive strength:2000 MpaBending strength:350 Mpa
Thermal shock resistance :GoodMax serve temp:1750 ℃

Silicon Nitride Ceramics

下载捕鱼游戏Technical parameters:

Content:99%Density:3.25g/cm3
Compressive strength:1500 MpaBending strength:600 Mpa
Thermal shock resistance :GoodMax serve temp:1700 ℃

Boron Nitride Ceramics

Technical parameters:

Content:99%Density:2.05-2.20g/cm3
Compressive strength:200 MpaBending strength:
Thermal shock resistance :GoodMax serve temp:1600-3000℃

Quartz / Silica Ceramics

下载捕鱼游戏Technical parameters:

Content:99.9%Density:2.2-2.3g/cm3
Compressive strength:1100 MpaBending strength:67 Mpa
Thermal shock resistance :GoodMax serve temp:1750℃